Filaments: Difference between revisions

@@ Line 40: / Line 40: @@
 | Filament density g/cm³ || 1.21 || 1.05 || 0.99
 |-
-| Foaming rate || 0-120% || n/a || 0-110%
+| Foaming rate || 0-120 || n/a || 0-110
 |-
-| Vol. expansion ratio || 100-220% || 102% || 100-210%
+| Vol. expansion ratio || 100-220 || 102 || 100-210
 |-
 | Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97
 |-
-| Tensile strength MPa || || || 32±4
+| Tensile strength MPa || 24±2 || || 32±4
 |-
-| Breaking elongation rate || || || 5.1% ± 1.6%
+| Breaking elongation rate || 2.6±0.7 || || 5.1±1.6
 |-
-| Bending modulus MPa || || || 1510±120
+| Bending modulus MPa || 1690±120 || || 1510±120
 |-
-| Bending strength MPa || || || 58±6
+| Bending strength MPa || 45±4 || || 58±6
 |-
-| Impact strength kJ/m² || || || 32.0±2.5
+| Impact strength kJ/m² || 28.8±1.3  || || 32.0±2.5
 |-
-| Melt index g/10min || || || 1.56 ± 0.5
+| Melt index g/10min || 7.7±0.6 || || 1.56 ± 0.5
 |-
-| Melting temp C || || || 204
+| Melting temp C || 153 || || 204
 |-
-| Heat deflection temp C || || || 85
+| Heat deflection temp C || 53 || || 85
 |-
-| Vicat softening temp C || || || 80
+| Vicat softening temp C || 54 || || 80
 |-
 |}