==Bambu filaments parameter table==

{| wikiclass="table" border="1"

! Parameter !! PLA Aero !! ASA !! ASA Aero !! PC !! ABS !! ABS-GF !! PETG-Trans !! PETG-HF !! PA6-CF !! PPA-CF

! Parameter !! PLA Aero !! ASA !! ASA Aero !! PC !! ABS !! ABS-GF !! PETG-Trans !! PETG-HF !! PA6-CF !! PPA-CF !! PETG-HF

|-

| Print temp C || 210-260 || 240-270 || 240-280 || 250-270 || 240-270 || 240-270 || 230-260 || 230-260 || 260-290 || 280-310

| Print temp C || 210-260 || 240-270 || 240-280 || 250-270 || 240-270 || 240-270 || 230-260 || 230-260 || 260-290 || 280-310 || 230-260

|-

| Print speed mm/s || <180 || <250 || <150 || <300 || <300 || <180 || <220 || <300 || <100 || <100

| Print speed mm/s || <180 || <250 || <150 || <300 || <300 || <180 || <220 || <300 || <100 || <100 || <300

|-

| Flow rate ratio || 0.5-0.8 || 0.93-0.97 || 0.45-0.80 || || || || || || ||

| Flow rate ratio || 0.5-0.8 || 0.93-0.97 || 0.45-0.80 || || || || || || || ||

|-

| Filament density g/cm³ || 1.21 || 1.05 || 0.99 || 1.2 || 1.05 || 1.08 || 1.25 || 1.28 || 1.09 || 1.25

| Filament density g/cm³ || 1.21 || 1.05 || 0.99 || 1.2 || 1.05 || 1.08 || 1.25 || 1.28 || 1.09 || 1.25 || 1.28

|-

| Foaming rate || 0-120 || n/a || 0-110 || n/a || n/a || n/a || n/a || n/a || n/a || n/a

| Foaming rate || 0-120 || n/a || 0-110 || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a

|-

| Vol. expansion ratio || 100-220 || 102 || 100-210 || || || || || || ||

| Vol. expansion ratio || 100-220 || 102 || 100-210 || || || || || || || ||

|-

| Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || ||

| Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || || ||

|-

| Tensile strength MPa || 24±2 || 37±3 || 32±4 || 55±4 || 33±3 || 36±3 || 33±4 || 34±4 || 102±7 || 168±4

| Tensile strength MPa || 24±2 || 37±3 || 32±4 || 55±4 || 33±3 || 36±3 || 33±4 || 34±4 || 102±7 || 168±4 || 34±4

|-

| Breaking elongation rate || 2.6±0.7 || 9.2±1.4 || 5.1±1.6 || 3.8±0.3 || 10.5±1.0 || 6.3±1.2 || 8.2±1.3 || 8.6±1.2 || 5.8±1.6 || 3.2±0.4

| Breaking elongation rate || 2.6±0.7 || 9.2±1.4 || 5.1±1.6 || 3.8±0.3 || 10.5±1.0 || 6.3±1.2 || 8.2±1.3 || 8.6±1.2 || 5.8±1.6 || 3.2±0.4 || 8.6±1.2

|-

| Bending modulus MPa || 1690±120 || 1920±130 || 1510±120 || 2310±70 || 1880±110 || 2860±130 || 1610±130 || 2050±120 || 5460±280 || 9860±480

| Bending modulus MPa || 1690±120 || 1920±130 || 1510±120 || 2310±70 || 1880±110 || 2860±130 || 1610±130 || 2050±120 || 5460±280 || 9860±480 || 2050±120

|-

| Bending strength MPa || 45±4 || 65±5 || 58±6 || 108±4 || 62±4 || 68±4 || 68±3 || 64±3 || 151±8 || 208±6

| Bending strength MPa || 45±4 || 65±5 || 58±6 || 108±4 || 62±4 || 68±4 || 68±3 || 64±3 || 151±8 || 208±6 || 64±3

|-

| Impact strength kJ/m² || 28.8±1.3 || 41.0±2.3 || 32.0±2.5 || 34.8±2.1 || 39±3.6 || 14.5±1.5 || 37.4±3.3 || 31.5±2.2 || 40.3±2.5 || 41.7±2.8

| Impact strength kJ/m² || 28.8±1.3 || 41.0±2.3 || 32.0±2.5 || 34.8±2.1 || 39±3.6 || 14.5±1.5 || 37.4±3.3 || 31.5±2.2 || 40.3±2.5 || 41.7±2.8 || 31.5±2.2

|-

| Melt index g/10min || 7.7±0.6 || 7.0±0.8 || 1.56 ± 0.5 || 32.2±2.9 || 34.2±3.8 || 7.56±1.4 || 11.7±1.5 || 28.2±2.7 || 6.8±0.6 || 8.4±0.7

| Melt index g/10min || 7.7±0.6 || 7.0±0.8 || 1.56 ± 0.5 || 32.2±2.9 || 34.2±3.8 || 7.56±1.4 || 11.7±1.5 || 28.2±2.7 || 6.8±0.6 || 8.4±0.7 || 28.2±2.7

|-

| Melting temp C || 153 || 210 || 204 || 228 || 200 || 202 || 228 || 214 || 223 || 258

| Melting temp C || 153 || 210 || 204 || 228 || 200 || 202 || 228 || 214 || 223 || 258 || 214

|-

| Heat deflection temp C || 53 || 100 || 85 || 117 || 87 || 99 || 74 || 69 || 186 || 227

| Heat deflection temp C || 53 || 100 || 85 || 117 || 87 || 99 || 74 || 69 || 186 || 227 || 69

|-

| Vicat softening temp C || 54 || 106 || 80 || 119 || 94 || 103 || 79 || 70 || 212 || 232

| Vicat softening temp C || 54 || 106 || 80 || 119 || 94 || 103 || 79 || 70 || 212 || 232 || 70

|-

|}

Filaments: Difference between revisions

Dank (talk | contribs)

@@ Line 34: / Line 34: @@
 ==Bambu filaments parameter table==
 {| wikiclass="table" border="1"
-! Parameter !! PLA Aero !! ASA !! ASA Aero !! PC !! ABS !! ABS-GF !! PETG-Trans !! PETG-HF !! PA6-CF !! PPA-CF
+! Parameter !! PLA Aero !! ASA !! ASA Aero !! PC !! ABS !! ABS-GF !! PETG-Trans !! PETG-HF !! PA6-CF !! PPA-CF !! PETG-HF
 |-
-| Print temp C || 210-260 || 240-270 || 240-280 || 250-270 || 240-270 || 240-270 || 230-260 || 230-260 || 260-290 || 280-310
+| Print temp C || 210-260 || 240-270 || 240-280 || 250-270 || 240-270 || 240-270 || 230-260 || 230-260 || 260-290 || 280-310 || 230-260
 |-
-| Print speed mm/s || <180 || <250 || <150 || <300 || <300 || <180 || <220 || <300 || <100 || <100
+| Print speed mm/s || <180 || <250 || <150 || <300 || <300 || <180 || <220 || <300 || <100 || <100 || <300
 |-
-| Flow rate ratio || 0.5-0.8 || 0.93-0.97 || 0.45-0.80 || || || || || || ||
+| Flow rate ratio || 0.5-0.8 || 0.93-0.97 || 0.45-0.80 || || || || || || || ||
 |-
-| Filament density g/cm³ || 1.21 || 1.05 || 0.99 || 1.2 || 1.05 || 1.08 || 1.25 || 1.28 || 1.09 || 1.25
+| Filament density g/cm³ || 1.21 || 1.05 || 0.99 || 1.2 || 1.05 || 1.08 || 1.25 || 1.28 || 1.09 || 1.25 || 1.28
 |-
-| Foaming rate || 0-120 || n/a || 0-110 || n/a || n/a || n/a || n/a || n/a || n/a || n/a
+| Foaming rate || 0-120 || n/a || 0-110 || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a
 |-
-| Vol. expansion ratio || 100-220 || 102 || 100-210 || || || || || || ||
+| Vol. expansion ratio || 100-220 || 102 || 100-210 || || || || || || || ||
 |-
-| Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || ||
+| Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || || ||
 |-
-| Tensile strength MPa || 24±2 || 37±3 || 32±4 || 55±4 || 33±3 || 36±3 || 33±4 || 34±4 || 102±7  || 168±4
+| Tensile strength MPa || 24±2 || 37±3 || 32±4 || 55±4 || 33±3 || 36±3 || 33±4 || 34±4 || 102±7  || 168±4 || 34±4
 |-
-| Breaking elongation rate || 2.6±0.7 || 9.2±1.4 || 5.1±1.6 || 3.8±0.3 || 10.5±1.0 || 6.3±1.2 || 8.2±1.3 || 8.6±1.2 || 5.8±1.6 || 3.2±0.4
+| Breaking elongation rate || 2.6±0.7 || 9.2±1.4 || 5.1±1.6 || 3.8±0.3 || 10.5±1.0 || 6.3±1.2 || 8.2±1.3 || 8.6±1.2 || 5.8±1.6 || 3.2±0.4 || 8.6±1.2
 |-
-| Bending modulus MPa || 1690±120 || 1920±130 || 1510±120 || 2310±70 || 1880±110 || 2860±130 || 1610±130 || 2050±120 || 5460±280 || 9860±480
+| Bending modulus MPa || 1690±120 || 1920±130 || 1510±120 || 2310±70 || 1880±110 || 2860±130 || 1610±130 || 2050±120 || 5460±280 || 9860±480 || 2050±120
 |-
-| Bending strength MPa || 45±4 || 65±5 || 58±6 || 108±4 || 62±4 || 68±4 || 68±3 || 64±3 || 151±8 || 208±6
+| Bending strength MPa || 45±4 || 65±5 || 58±6 || 108±4 || 62±4 || 68±4 || 68±3 || 64±3 || 151±8 || 208±6 || 64±3
 |-
-| Impact strength kJ/m² || 28.8±1.3 || 41.0±2.3 || 32.0±2.5 || 34.8±2.1 || 39±3.6 || 14.5±1.5 || 37.4±3.3 || 31.5±2.2 || 40.3±2.5 || 41.7±2.8
+| Impact strength kJ/m² || 28.8±1.3 || 41.0±2.3 || 32.0±2.5 || 34.8±2.1 || 39±3.6 || 14.5±1.5 || 37.4±3.3 || 31.5±2.2 || 40.3±2.5 || 41.7±2.8 || 31.5±2.2
 |-
-| Melt index g/10min || 7.7±0.6 || 7.0±0.8 || 1.56 ± 0.5 || 32.2±2.9 || 34.2±3.8 || 7.56±1.4 || 11.7±1.5 || 28.2±2.7 || 6.8±0.6 || 8.4±0.7
+| Melt index g/10min || 7.7±0.6 || 7.0±0.8 || 1.56 ± 0.5 || 32.2±2.9 || 34.2±3.8 || 7.56±1.4 || 11.7±1.5 || 28.2±2.7 || 6.8±0.6 || 8.4±0.7 || 28.2±2.7
 |-
-| Melting temp C || 153 || 210 || 204 || 228 || 200 || 202 || 228 || 214 || 223 || 258
+| Melting temp C || 153 || 210 || 204 || 228 || 200 || 202 || 228 || 214 || 223 || 258 || 214
 |-
-| Heat deflection temp C || 53 || 100 || 85 || 117 || 87 || 99 || 74 || 69 || 186 || 227
+| Heat deflection temp C || 53 || 100 || 85 || 117 || 87 || 99 || 74 || 69 || 186 || 227 || 69
 |-
-| Vicat softening temp C || 54 || 106 || 80 || 119 || 94 || 103 || 79 || 70 || 212 || 232
+| Vicat softening temp C || 54 || 106 || 80 || 119 || 94 || 103 || 79 || 70 || 212 || 232 || 70
 |-
 |}