Filaments: Difference between revisions
| Line 54: | Line 54: | ||
| Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || || || || | | Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || || || || | ||
|- | |- | ||
| Tensile strength MPa || | | Tensile strength MPa || 24 ± 2 || 37 ± 3 || 32 ± 4 || 55 ± 4 || 33 ± 3 || 36 ± 3 || 33 ± 4 || 34 ± 4 || 102 ± 7 || 168 ± 4 || 38 ± 4 || 87 ± 5 | ||
|- | |- | ||
| Breaking elongation rate || 2. | | Breaking elongation rate || 2.6 ± 0.7 || 9.2 ± 1.4 || 5.1 ± 1.6 || 3.8 ± 0.3 || 10.5 ± 1.0 || 6.3 ± 1.2 || 8.2 ± 1.3 || 8.6 ± 1.2 || 5.8 ± 1.6 || 3.2 ± 0.4 || 8.4 ± 3.2 || 1.2 ± 0.4 | ||
|- | |- | ||
| Bending modulus MPa || | | Bending modulus MPa || 1690 ± 120 || 1920 ± 130 || 1510 ± 120 || 2310 ± 70 || 1880 ± 110 || 2860 ± 130 || 1610 ± 130 || 2050 ± 120 || 5460 ± 280 || 9860 ± 480 || 3950 ± 190 || 7160 ± 280 | ||
|- | |- | ||
| Bending strength MPa || | | Bending strength MPa || 45 ± 4 || 65 ± 5 || 58 ± 6 || 108 ± 4 || 62 ± 4 || 68 ± 4 || 68 ± 3 || 64 ± 3 || 151 ± 8 || 208 ± 6 || 89 ± 4 || 142 ± 5 | ||
|- | |- | ||
| Impact strength kJ/m² || 28. | | Impact strength kJ/m² || 28.8 ± 1.3 || 41.0 ± 2.3 || 32.0 ± 2.5 || 34.8 ± 2.1 || 39 ± 3.6 || 14.5 ± 1.5 || 37.4 ± 3.3 || 31.5 ± 2.2 || 40.3 ± 2.5 || 41.7 ± 2.8 || 23.2 ± 3.7 || 27.8 ± 2.3 | ||
|- | |- | ||
| Melt index g/10min || 7. | | Melt index g/10min || 7.7 ± 0.6 || 7.0 ± 0.8 || 1.56 ± 0.5 || 32.2 ± 2.9 || 34.2 ± 3.8 || 7.56 ± 1.4 || 11.7 ± 1.5 || 28.2 ± 2.7 || 6.8 ± 0.6 || 8.4 ± 0.7 || 3.7 ± 0.6 || 11.48 ± 1.23 | ||
|- | |- | ||
| Melting temp ℃ || 153 || 210 || 204 || 228 || 200 || 202 || 228 || 214 || 223 || 258 || 165 || 284 | | Melting temp ℃ || 153 || 210 || 204 || 228 || 200 || 202 || 228 || 214 || 223 || 258 || 165 || 284 | ||