==Bambu filaments parameter table==
==Bambu filaments parameter table==
{| class="wikitable" border="1"
{| class="wikitable" border="1"
! Parameter !! PLA Aero !! ASA !! ASA Aero !! PC !! ABS !! ABS-GF !! PETG-Trans !! PETG-HF !! PA6-CF !! PPA-CF !! PLA-CF !! PPS-CF
! Parameter !! PLA Aero !! ASA !! ASA Aero !! PC !! ABS !! ABS-GF !! PETG-Trans !! PETG-HF !! PA6-CF !! PPA-CF !! PLA-CF !! PPS-CF !! PAHT-CF
|-
|-
| Print temp ℃ || 210-260 || 240-270 || 240-280 || 250-270 || 240-270 || 240-270 || 230-260 || 230-260 || 260-290 || 280-310 || 210-240 || 310-340
| Print temp ℃ || 210-260 || 240-270 || 240-280 || 250-270 || 240-270 || 240-270 || 230-260 || 230-260 || 260-290 || 280-310 || 210-240 || 310-340 || 260-290
|-
|-
| Print speed mm/s || <180 || <250 || <150 || <300 || <300 || <180 || <220 || <300 || <100 || <100 || <200 || <100
| Print speed mm/s || <180 || <250 || <150 || <300 || <300 || <180 || <220 || <300 || <100 || <100 || <200 || <100 || <100
|-
|-
| Flow rate ratio || 0.5-0.8 || 0.93-0.97 || 0.45-0.80 || || || || || || || || ||
| Flow rate ratio || 0.5-0.8 || 0.93-0.97 || 0.45-0.80 || || || || || || || || || ||
|-
|-
| Filament density g/cm³ || 1.21 || 1.05 || 0.99 || 1.2 || 1.05 || 1.08 || 1.25 || 1.28 || 1.09 || 1.25 || 1.22 || 1.26
| Filament density g/cm³ || 1.21 || 1.05 || 0.99 || 1.2 || 1.05 || 1.08 || 1.25 || 1.28 || 1.09 || 1.25 || 1.22 || 1.26 || 1.06
|-
|-
| Foaming rate || 0-120 || n/a || 0-110 || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a
| Foaming rate || 0-120 || n/a || 0-110 || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a
|-
|-
| Vol. expansion ratio || 100-220 || 102 || 100-210 || || || || || || || || ||
| Vol. expansion ratio || 100-220 || 102 || 100-210 || || || || || || || || || ||
|-
|-
| Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || || || ||
| Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || || || || ||
|-
|-
| Tensile strength MPa || 24 ± 2 || 37 ± 3 || 32 ± 4 || 55 ± 4 || 33 ± 3 || 36 ± 3 || 33 ± 4 || 34 ± 4 || 102 ± 7  || 168 ± 4 || 38 ± 4 || 87 ± 5  
| Tensile strength MPa || 24 ± 2 || 37 ± 3 || 32 ± 4 || 55 ± 4 || 33 ± 3 || 36 ± 3 || 33 ± 4 || 34 ± 4 || 102 ± 7  || 168 ± 4 || 38 ± 4 || 87 ± 5 || 92 ± 7
|-
|-
| Breaking elongation rate || 2.6 ± 0.7 || 9.2 ± 1.4 || 5.1 ± 1.6 || 3.8 ± 0.3 || 10.5 ± 1.0 || 6.3 ± 1.2 || 8.2 ± 1.3 || 8.6 ± 1.2 || 5.8 ± 1.6 || 3.2 ± 0.4 || 8.4 ± 3.2 || 1.2 ± 0.4
| Breaking elongation rate || 2.6 ± 0.7 || 9.2 ± 1.4 || 5.1 ± 1.6 || 3.8 ± 0.3 || 10.5 ± 1.0 || 6.3 ± 1.2 || 8.2 ± 1.3 || 8.6 ± 1.2 || 5.8 ± 1.6 || 3.2 ± 0.4 || 8.4 ± 3.2 || 1.2 ± 0.4 || 8.4 ± 1.8
|-
|-
| Bending modulus MPa || 1690 ± 120 || 1920 ± 130 || 1510 ± 120 || 2310 ± 70 || 1880 ± 110 || 2860 ± 130 || 1610 ± 130 || 2050 ± 120 || 5460 ± 280 || 9860 ± 480 || 3950 ± 190 || 7160 ± 280
| Bending modulus MPa || 1690 ± 120 || 1920 ± 130 || 1510 ± 120 || 2310 ± 70 || 1880 ± 110 || 2860 ± 130 || 1610 ± 130 || 2050 ± 120 || 5460 ± 280 || 9860 ± 480 || 3950 ± 190 || 7160 ± 280 || 4230 ± 210
|-
|-
| Bending strength MPa || 45 ± 4 || 65 ± 5 || 58 ± 6 || 108 ± 4 || 62 ± 4 || 68 ± 4 || 68 ± 3 || 64 ± 3 || 151 ± 8 || 208 ± 6 || 89 ± 4 || 142 ± 5
| Bending strength MPa || 45 ± 4 || 65 ± 5 || 58 ± 6 || 108 ± 4 || 62 ± 4 || 68 ± 4 || 68 ± 3 || 64 ± 3 || 151 ± 8 || 208 ± 6 || 89 ± 4 || 142 ± 5 || 125 ± 7
|-
|-
| Impact strength kJ/m² || 28.8 ± 1.3 || 41.0 ± 2.3 || 32.0 ± 2.5 || 34.8 ± 2.1 || 39 ± 3.6 || 14.5 ± 1.5 || 37.4 ± 3.3 || 31.5 ± 2.2 || 40.3 ± 2.5 || 41.7 ± 2.8 || 23.2 ± 3.7 || 27.8 ± 2.3
| Impact strength kJ/m² || 28.8 ± 1.3 || 41.0 ± 2.3 || 32.0 ± 2.5 || 34.8 ± 2.1 || 39 ± 3.6 || 14.5 ± 1.5 || 37.4 ± 3.3 || 31.5 ± 2.2 || 40.3 ± 2.5 || 41.7 ± 2.8 || 23.2 ± 3.7 || 27.8 ± 2.3 || 57.5 ± 3.4
|-
|-
| Melt index g/10min || 7.7 ± 0.6 || 7.0 ± 0.8 || 1.56  ±  0.5 || 32.2 ± 2.9 || 34.2 ± 3.8 || 7.56 ± 1.4 || 11.7 ± 1.5 || 28.2 ± 2.7 || 6.8 ± 0.6 || 8.4 ± 0.7 || 3.7 ± 0.6 || 11.48 ± 1.23
| Melt index g/10min || 7.7 ± 0.6 || 7.0 ± 0.8 || 1.56  ±  0.5 || 32.2 ± 2.9 || 34.2 ± 3.8 || 7.56 ± 1.4 || 11.7 ± 1.5 || 28.2 ± 2.7 || 6.8 ± 0.6 || 8.4 ± 0.7 || 3.7 ± 0.6 || 11.48 ± 1.23 || 14.4 ± 2.0
|-
|-
| Melting temp ℃ || 153 || 210 || 204 || 228 || 200 || 202 || 228 || 214 || 223 || 258 || 165 || 284
| Melting temp ℃ || 153 || 210 || 204 || 228 || 200 || 202 || 228 || 214 || 223 || 258 || 165 || 284 || 225
|-
|-
| Heat deflection temp ℃ || 53 || 100 || 85 || 117 || 87 || 99 || 74 || 69 || 186 || 227 || 55 || 264
| Heat deflection temp ℃ || 53 || 100 || 85 || 117 || 87 || 99 || 74 || 69 || 186 || 227 || 55 || 264 || 194
|-
|-
| Vicat softening temp ℃ || 54 || 106 || 80 || 119 || 94 || 103 || 79 || 70 || 212 || 232 || 69 || 268
| Vicat softening temp ℃ || 54 || 106 || 80 || 119 || 94 || 103 || 79 || 70 || 212 || 232 || 69 || 268 || 220
|-
|-
|}
|}