Line 40:

! Parameter !! PLA Aero !! ASA !! ASA Aero !! PC !! ABS !! ABS-GF !! PETG-Trans !! PETG-HF !! PA6-CF !! PPA-CF !! PLA-CF !! PPS-CF !! PAHT-CF !! ASA-CF

|-

| Print temp ℃ || 210-260 || 240-270 || 240-280 || 250-270 || 240-270 || 240-270 || 230-260 || 230-260 || 260-290 || 280-310 || 210-240 || 310-340 || 260-290 || 250-280

| Print temp ℃ || 210 - 260 || 240 - 270 || 240 - 280 || 250 - 270 || 240 - 270 || 240 - 270 || 230 - 260 || 230 - 260 || 260 - 290 || 280 - 310 || 210 - 240 || 310 - 340 || 260 - 290 || 250 - 280

|-

| Print speed mm/s || <180 || <250 || <150 || <300 || <300 || <180 || <220 || <300 || <100 || <100 || <200 || <100 || <100 || <250

Line 50:

| Foaming rate || 0-120 || n/a || 0-110 || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a

|-

| Vol. expansion ratio || 100-220 || 102 || 100-210 || || || || || || || || || || ||

| Vol. expansion ratio || 100 - 220 || 102 || 100 - 210 || || || || || || || || || || ||

|-

| Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || || || || || ||

| Print density g/cm³ || 0.55 - 1.05 || 1.03 || 0.46 - 0.97 || || || || || || || || || || ||

|-

| Tensile strength MPa || 24 ± 2 || 37 ± 3 || 32 ± 4 || 55 ± 4 || 33 ± 3 || 36 ± 3 || 33 ± 4 || 34 ± 4 || 102 ± 7 || 168 ± 4 || 38 ± 4 || 87 ± 5 || 92 ± 7 || 34 ± 3

Filaments: Difference between revisions

Dank (talk | contribs)

@@ Line 40: / Line 40: @@
 ! Parameter !! PLA Aero !! ASA !! ASA Aero !! PC !! ABS !! ABS-GF !! PETG-Trans !! PETG-HF !! PA6-CF !! PPA-CF !! PLA-CF !! PPS-CF !! PAHT-CF !! ASA-CF
 |-
-| Print temp ℃ || 210-260 || 240-270 || 240-280 || 250-270 || 240-270 || 240-270 || 230-260 || 230-260 || 260-290 || 280-310 || 210-240 || 310-340 || 260-290 || 250-280
+| Print temp ℃ || 210 - 260 || 240 - 270 || 240 - 280 || 250 - 270 || 240 - 270 || 240 - 270 || 230 - 260 || 230 - 260 || 260 - 290 || 280 - 310 || 210 - 240 || 310 - 340 || 260 - 290 || 250 - 280
 |-
 | Print speed mm/s || <180 || <250 || <150 || <300 || <300 || <180 || <220 || <300 || <100 || <100 || <200 || <100 || <100 || <250
@@ Line 50: / Line 50: @@
 | Foaming rate || 0-120 || n/a || 0-110 || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a || n/a
 |-
-| Vol. expansion ratio || 100-220 || 102 || 100-210 || || || || || || || || || || ||
+| Vol. expansion ratio || 100 - 220 || 102 || 100 - 210 || || || || || || || || || || ||
 |-
-| Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97 || || || || || || || || || || ||
+| Print density g/cm³ || 0.55 - 1.05 || 1.03 || 0.46 - 0.97 || || || || || || || || || || ||
 |-
 | Tensile strength MPa || 24 ± 2 || 37 ± 3 || 32 ± 4 || 55 ± 4 || 33 ± 3 || 36 ± 3 || 33 ± 4 || 34 ± 4 || 102 ± 7  || 168 ± 4 || 38 ± 4 || 87 ± 5 || 92 ± 7 || 34 ± 3