Filaments: Difference between revisions

@@ Line 46: / Line 46: @@
 | Print density g/cm³ || 0.55-1.05 || 1.03 || 0.46-0.97
 |-
-| Tensile strength MPa || 24±2 || || 32±4
+| Tensile strength MPa || 24±2 || 37±3 || 32±4
 |-
-| Breaking elongation rate || 2.6±0.7 || || 5.1±1.6
+| Breaking elongation rate || 2.6±0.7 || 9.2±1.4 || 5.1±1.6
 |-
-| Bending modulus MPa || 1690±120 || || 1510±120
+| Bending modulus MPa || 1690±120 || 1920±130 || 1510±120
 |-
-| Bending strength MPa || 45±4 || || 58±6
+| Bending strength MPa || 45±4 || 65±5 || 58±6
 |-
-| Impact strength kJ/m² || 28.8±1.3  || || 32.0±2.5
+| Impact strength kJ/m² || 28.8±1.3 || 41.0±2.3 || 32.0±2.5
 |-
-| Melt index g/10min || 7.7±0.6 || || 1.56 ± 0.5
+| Melt index g/10min || 7.7±0.6 || 7.0±0.8 || 1.56 ± 0.5
 |-
-| Melting temp C || 153 || || 204
+| Melting temp C || 153 || 210 || 204
 |-
-| Heat deflection temp C || 53 || || 85
+| Heat deflection temp C || 53 || 100 || 85
 |-
-| Vicat softening temp C || 54 || || 80
+| Vicat softening temp C || 54 || 106 || 80
 |-
 |}