Keeping notes on various FDM printing filaments here. Prices are per kilogram spool unless stated otherwise. Printing was done on a Bambu Carbon X1C unless stated otherwise.

Polylactic acid (PLA)

  • Bambu silky green 2024-06 $25: beautiful results

Thermoplastic polyurethane (TPU)

  • Overture 95A green 2024-06 $30: stringy as hell

Acrylonitrile butadiene styrene (ABS)

  • Bambu black/green 2024-06 $14 (4kg @ $56): solid workhorse

High impact polystyrene (HIPS)

Support material for ABS/PET, dissolvable

  • Bambu green Support-G $80 ($40/.5kg): expensive!

Acrylic styrene acrylonitrile (ASA)

  • Atomic Filaments black 2024-06 $19 (7kg @ $130): lay the first layer at 105, and remaining layers at 115.

Polycarbonate (PC)

  • Bambu clear black 2024-06 $40: befouled my .4mm hotend. Very lovely when it prints.
    • warping at 115, stick to builtin 110

Polyamide Nylon (PA)

  • Atomic Filaments black

Polyethylene terephthalate (PET)

Polyethylene terephthalate glycol (PETG)

  • Atomic Filaments black Carbon Fiber: result is very tough
  • Bambu Support-W (breakaway PLA support) $70 ($35/.5kg): works well enough, expensive

Bambu filaments parameter table

Parameter PLA Aero ASA ASA Aero PC ABS ABS-GF
Print temp C 210-260 240-270 240-280 250-270 240-270 240-270
Print speed mm/s <180 <250 <150 <300 <300 <180
Flow rate ratio 0.5-0.8 0.93-0.97 0.45-0.80
Filament density g/cm³ 1.21 1.05 0.99 1.2 1.05 1.08
Foaming rate 0-120 n/a 0-110 n/a n/a n/a
Vol. expansion ratio 100-220 102 100-210
Print density g/cm³ 0.55-1.05 1.03 0.46-0.97
Tensile strength MPa 24±2 37±3 32±4 55±4 33±3 36±3
Breaking elongation rate 2.6±0.7 9.2±1.4 5.1±1.6 3.8±0.3 10.5±1.0 6.3±1.2
Bending modulus MPa 1690±120 1920±130 1510±120 2310±70 1880±110 2860±130
Bending strength MPa 45±4 65±5 58±6 108±4 62±4 68±4
Impact strength kJ/m² 28.8±1.3 41.0±2.3 32.0±2.5 34.8±2.1 39±3.6 14.5±1.5
Melt index g/10min 7.7±0.6 7.0±0.8 1.56 ± 0.5 32.2±2.9 34.2±3.8 7.56±1.4
Melting temp C 153 210 204 228 200 202
Heat deflection temp C 53 100 85 117 87 99
Vicat softening temp C 54 106 80 119 94 103